Superlit - 'F'
|
|
|
TECHNICAL DATA SHEET |
| Basis |
| Chrysotile asbestos fibre, Nitrile Butadiene Rubber |
| General properties and applications : |
To seal off motor oil, carburetor mixtures, hydraulic fluids, low temperature oils, steam, alkalies and water/antifreeze and water/anticorrosion mixtures. This grade offers high oil and fuel resistance. |
| Dimensions of standard sheets : |
| Standard sheet sizes : 1500 mm X 1500 mm, 1500 mm X 4500 mm,
1500 mm X 1125 mm, 1500 mm X 1000 mm, 1500 mm x 2000 mm,1500
mm X 4000 |
| Thickness: 0.25mm, 0.50mm, 0.75mm, 1mm, 1.5mm, 2mm, 3mm, 4mm, 5mm, 6mm |
| (other sheet thickness on requirement). |
| Finish : Grey |
| Technical data |
| All data are typical values and refer to sheet thickness of 1.5 mm |
|
Specification |
| |
|
|
|
| Max. Operating Temperature |
|
450 |
°C |
| Max. Operating Pressure |
|
50 |
bar |
| Density |
ASTM F 1315 |
1.9 |
g/cm³ |
| Compressibility |
ASTM F 36 A |
8
|
% |
| Recovery |
ASTM F 36 A |
50 |
% |
| Tensile Strength |
ASTM F 152 |
25 |
N/mm² |
| Stress Relaxation (50 N/mm²,16h,300°C) |
DIN 52913 |
28
|
N/mm² |
| Loss on ignition |
ASTM F 495 |
24 |
% |
| Thickness increase |
ASTM F 146 |
|
| ASTM oil no.3 (5h, 150°C) |
|
10 |
% |
| ASTM Fuel B (5h, 23 °C) |
|
10 |
% |
| Weight Increase |
ASTM F 146 |
|
|
| ASTM oil no.3 (5h, 150°C) |
|
15 |
% |
| ASTM Fuel B (5h, 23 °C) |
|
10 |
% |
| Water (48h, 23 °C) |
|
5 |
% |
All information and recommendations given in this brochure are correct to the best of our knowledge. However, in view of the wide varity of possible installation and operating conditions one cannot draw the final conclusion in all application cases regarding the behaviour in a gasket joint. Therefore, information can only serve as a guideline. |
SUPERLITE JOINTINGS PVT. LTD.
An ISO/TS 16949:2002 Company
Manufacturer of asbestos and asbestos free jointing materials
D-6, Sec.-17, Kavi Nagar Ind. Area Ghaziabad-201002(U.P.) INDIA
Phone : +91-120-2705280, Fax : +91-120-2703880
Website : www.superlitejointings.com |
|
|
|
|
|
|
|
|
|
|
|
|
|
|